Pwopriyete REFRACTORY nan brik Corundum
As shown in the Al2O3-Cr2O3 binary phase diagram, Al2O3 and Cr2O3 can form a continuous solid solution without the formation of eutectic. Therefore, adding Cr2O3 to high-purity corundum materials, regardless of the amount added, not only does not reduce the material's refractory properties, but actually improves them. The refractoriness (>1790 ℃) and load softening temperature (>1700 degre ) nan kwòm korundum brik yo siperyè ak sa yo ki gen gwo -pite pwodwi korundum.
Fòs nan brik Corundum
The room temperature compressive strength of high-purity corundum bricks is generally 70–100 MPa, while the room temperature compressive strength of high-performance chromium corundum bricks is generally >150 MPa, siyifikativman pi wo pase sa yo ki nan brik korundum regilye. Sa a se paske pandan pwosesis la tire, solisyon solid Al2O3-Cr2O3 fòme ant patikil, ant patikil ak poud amann, ak ant poud amann tèt yo. Solisyon solid sa yo aji tankou pon, konekte patikil yo ak poud amann, ogmante siyifikativman fòs materyèl la.
Estabilite chòk tèmik
Selon rapò, lè yo ajoute Cr2O3 nan korundon, estabilite chòk tèmik la diminye ak ogmante kontni Cr2O3, espesyalman lè kontni Cr2O3 se ant 10% ak 66%. Nan lòt mo, chromium korundum brik ki gen kontni ki ba Cr2O3 gen pi bon estabilite chòk tèmik pase sa yo ki gen gwo kontni Cr2O3.
Rezistans ewozyon salop
Solibilite nan divès oksid refractory nan salop chabon fonn: Solibilite nan Cr2O3 nan salop gazeifikasyon chabon (SiO2-sistèm CaO) ak divès kalite fonn vè se pi ba anpil pase sa yo ki nan lòt materyèl oksid. Se poutèt sa, Cr2O3 oswa Cr2O3 ki gen materyèl refractory gen bon rezistans nan korozyon soti nan salop asye, salop ki pa FERROUS SMELTING, salop gazeifikasyon chabon, salop gazeifikasyon lwil oliv ak divès kalite fonn vè.